Al composition dependent properties of quaternary AlInGaN Schottky diodes

Y. Liu, H. Jiang, T. Egawa, B. Zhang, H. Ishikawa

Research output: Contribution to journalArticlepeer-review

9 Citations (Scopus)


Pd Schottky barrier diodes were fabricated on undoped AlxIn 0.02Ga0.98-xN/GaN with x less than 20%. The material properties, which were characterized by photoluminescence, x-ray diffraction, and atomic force microscopy, indicated that the quaternary samples were coherently grown on GaN template with high crystalline quality. The flatband barrier height obtained by capacitance-voltage (C-V) measurement increased with increasing Al mole fraction (increasing the band gap of the quaternary) up to 2.06 eV, in agreement with the predictions of the Schottky-Mott theory. However, current-voltage (I-V) measurements revealed that the barrier height decreased from 1.32 to 1.12 eV, which was accompanied by an increase in ideality factor from 1.04 to 1.73. The large difference of barrier height between I-V and C-V measurements could not be quantitatively explained by the traditional electron transport mechanisms of Schottky diode, such as tunneling effect, image force effect, and barrier inhomogeneity theory. Strong polarization effect in strained AlxIn0.02Ga0.98-xN/GaN heterostructure was proposed to account for the experimental results, since similar phenomena had been observed extensively in strained AlyGa1-yN/GaN heterojunction structures.

Original languageEnglish
Article number123702
JournalJournal of Applied Physics
Issue number12
Publication statusPublished - 2006
Externally publishedYes

ASJC Scopus subject areas

  • General Physics and Astronomy


Dive into the research topics of 'Al composition dependent properties of quaternary AlInGaN Schottky diodes'. Together they form a unique fingerprint.

Cite this