TY - JOUR
T1 - Annealing effects on the Meissner signals from HgBaCaCuO superconductors
AU - Adachi, Seiji
AU - Tokiwa-Yamamoto, Ayako
AU - Itoh, Makoto
AU - Isawa, Kazuyuki
AU - Yamauchi, H.
N1 - Funding Information:
The authors would like to express their gratitude to S. Tanaka (SRL-ISTEC) for his continuous encouragement. This work was supported by NEDO for the Industrial Science and Technology Frontier Program.
PY - 1993/9/10
Y1 - 1993/9/10
N2 - As-sintered samples of the HgBaCaCuO superconductors were annealed in flowing argon, flowing oxygen and high-pressure oxygen gases. The superconducting critical temperature, Tc, of the sample increased after annealing in either flowing oxygen or a high-pressure oxygen gas, while it decreased after annealing in flowing argon. These results indicated that the as-sintered samples were in slightly "under-doped" states.
AB - As-sintered samples of the HgBaCaCuO superconductors were annealed in flowing argon, flowing oxygen and high-pressure oxygen gases. The superconducting critical temperature, Tc, of the sample increased after annealing in either flowing oxygen or a high-pressure oxygen gas, while it decreased after annealing in flowing argon. These results indicated that the as-sintered samples were in slightly "under-doped" states.
UR - http://www.scopus.com/inward/record.url?scp=0027657041&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0027657041&partnerID=8YFLogxK
U2 - 10.1016/0921-4534(93)90832-B
DO - 10.1016/0921-4534(93)90832-B
M3 - Article
AN - SCOPUS:0027657041
SN - 0921-4534
VL - 214
SP - 313
EP - 315
JO - Physica C: Superconductivity and its applications
JF - Physica C: Superconductivity and its applications
IS - 3-4
ER -