Cattail leaf-derived nitrogen-doped carbons via hydrothermal ammonia treatment for electrocatalytic oxygen reduction in an alkaline electrolyte

Gasidit Panomsuwan, Apiluck Eiad-ua, Napat Kaewtrakulchai, Ai Seizawa, Takahiro Ishizaki

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)


Cattail leaf-derived nitrogen-doped carbons (CL-NCs) were prepared by hydrothermal treatment in ammonia solution and subsequent pyrolysis for application as catalysts for the oxygen reduction reaction (ORR). The ammonia concentration was varied at 1.0, 1.5, and 2.0 M to alter the nitrogen doping content. The characterization results revealed that CL-NCs exhibited an amorphous structure, while the density of structural defects increased as the ammonia concentration increased. The CL-NC prepared without hydrothermal ammonia treatment had a nonporous structure with a low specific surface area (5 m2 g−1). With hydrothermal ammonia treatment, CL-NCs exhibited a micro–mesoporous structure with a higher surface area (113–496 m2 g−1); however, the surface area was significantly diminished at higher ammonia concentrations due to the deterioration of the pore structure. The nitrogen-doping content in CL-NCs varied from 0.65 to 1.55 atom% with the predominant ratios of pyridinic-N and graphitic-N. For electrochemical evaluation in an alkaline electrolyte (0.1 M KOH), CL-NC prepared at an ammonia concentration of 1.0 M showed the highest ORR activity among all samples, as indicated by the most positive onset potential (−0.05 V vs. Ag/AgCl) and half-wave potential (−0.22 V vs. Ag/AgCl) as well as the highest diffusion-limiting current density with a more favorable reduction via a direct four-electron pathway (n = 3.23–3.52). The ORR activity of CL-NCs had a similar trend to their specific surface area rather than nitrogen doping content, indicating the important role of surface area and porosity in enhancing the ORR activity. Moreover, it possessed excellent stability under long-term operation and exposure to methanol. The results obtained in this work could be helpful information for the further development and utilization of biomass-derived NCs for ORR catalysts.

Original languageEnglish
Pages (from-to)24738-24749
Number of pages12
JournalInternational Journal of Hydrogen Energy
Issue number59
Publication statusPublished - 2022 Jul 12


  • Biomass
  • Cattail leaves
  • Electrocatalysts
  • Hydrothermal ammonia treatment
  • Nitrogen-doped carbons
  • Oxygen reduction reaction

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology


Dive into the research topics of 'Cattail leaf-derived nitrogen-doped carbons via hydrothermal ammonia treatment for electrocatalytic oxygen reduction in an alkaline electrolyte'. Together they form a unique fingerprint.

Cite this