Epoxy-embedded silver nanowire meshes for transparent flexible electrodes

Lei Miao, Guojun Liu, Kevin McEleney, Jiandong Wang

Research output: Contribution to journalArticlepeer-review

18 Citations (Scopus)


Spreading a Ag nanowire (NW) dispersion using a bar coater onto a poly(ethylene terephthalate) (PET) film and evaporating the solvent yielded a transparent NW mesh. Further spreading a solution of bisphenol A diglycidyl ether and hardeners over this mesh using the bar coater and curing the epoxy precursors produced an epoxy-embedded NW mesh or an embedded NW electrode. Various techniques including scanning electron microscopy, transmission electron microscopy, and measurements of sheet resistance and transmittance were used to monitor the electrode fabrication process, which involved NW synthesis, casting NWs onto PET or glass substrates, subjecting the NW mesh to plasma treatment, and mesh embedment by an epoxy. Using our casting method, the areal density of the spread NWs and the thickness of the epoxy layer could be readily tuned by changing the concentrations of the NW dispersion and the epoxy precursory solution concentration, respectively. Our optimized electrodes had a Ag mass density of 1.0 × 10 −5  g/cm 2 in the NW mesh, embedded in an epoxy layer with a thickness of 0.6 µm. While many of the NW junctions in the mesh were locked in the coating matrix, sections of the NWs were arched over the epoxy layer to provide the required electrical contact with external devices. The optimized electrodes had a sheet resistance R s value of 18.9 ± 4.8 Ω/□ and a transmittance (T%) of 86.5 ± 0.3% at 550 nm. In addition, the embedded electrode withstood 500 cycles of bending, 500 repetitions of rubbing, and over 100 cycles of an adhesion tape test without noticeable deteriorations in their R s and T% values. Furthermore, their high-temperature stability and sulfurization resistance were significantly enhanced over those of the unembedded electrodes and they also withstood soaking in ethanol and acetone. The ready availability and affordability of the epoxy formulation and the high control of the epoxy deposition protocol suggest that this electrode fabrication strategy has significant practical value.

Original languageEnglish
Pages (from-to)10355-10370
Number of pages16
JournalJournal of Materials Science
Issue number14
Publication statusPublished - 2019 Jul 30
Externally publishedYes

ASJC Scopus subject areas

  • General Materials Science
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Epoxy-embedded silver nanowire meshes for transparent flexible electrodes'. Together they form a unique fingerprint.

Cite this