T1 - Fabrication of large melt-textured RE-Ba-Cu-O (RE = Gd, Dy) superconductors and their trapped magnetic fields
AU - Nariki, Shinya
AU - Sakai, Naomichi
AU - Murakami, Masato
N1 - Funding Information:
This work is supported by the New Energy and Industrial Technology Development Organization (NEDO) as Collaborative Research and Development of Fundamental Technologies for Superconductivity Applications under the New Sunshine Program administered by the Agency of Industrial Science and Technology (AIST) of the Ministry of International Trade and Industry (MITI) of Japan.
PY - 2001
Y1 - 2001
N2 - We have succeeded in synthesizing RE-Ba-Cu-O (RE = Gd and Dy) bulk superconductors with excellent field trapping properties. Large c-axis oriented single-domain Gd-Ba-Cu-O bulk samples with Ag addition were melt-textured under controlled oxygen partial pressure of 1.0%. The Gd-Ba-Cu-O sample 50 mm in diameter could trap a high flux density of 2.4 T at 77 K. In addition, we measured the trapped field between two Gd-bulks in order to minimize the demagnetizing effect and found that it reached 3.3 T. The single-domain Dy-Ba-Cu-O/Ag bulk 48 mm in diameter was also fabricated in air and its trapped field was 1.9 T at 77 K.
AB - We have succeeded in synthesizing RE-Ba-Cu-O (RE = Gd and Dy) bulk superconductors with excellent field trapping properties. Large c-axis oriented single-domain Gd-Ba-Cu-O bulk samples with Ag addition were melt-textured under controlled oxygen partial pressure of 1.0%. The Gd-Ba-Cu-O sample 50 mm in diameter could trap a high flux density of 2.4 T at 77 K. In addition, we measured the trapped field between two Gd-bulks in order to minimize the demagnetizing effect and found that it reached 3.3 T. The single-domain Dy-Ba-Cu-O/Ag bulk 48 mm in diameter was also fabricated in air and its trapped field was 1.9 T at 77 K.
UR - http://www.scopus.com/inward/record.url?scp=0035742594&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0035742594&partnerID=8YFLogxK
M3 - Conference article
AN - SCOPUS:0035742594
SN - 0272-9172
VL - 659
SP - II10.7.1-II10.7.5
JO - Materials Research Society Symposium - Proceedings
JF - Materials Research Society Symposium - Proceedings
T2 - High Temperature Superconductors - Crystal Chemistrym Processing and Properties
Y2 - 27 November 2000 through 1 December 2000
ER -