High-temperature oxidation process of intermetallic compound Ti-42 at% Al

Akito Takasaki, Kozo Ojima, Youji Taneda, Taiji Hoshiya, Akira Mitsuhashi

Research output: Contribution to journalArticlepeer-review

16 Citations (Scopus)


The oxidation process of two-phase (Ti3Al and TiAl) intermetallic compound, Ti-42 at% Al, in air at 1073 and 1273 K has been investigated. The oxidation at 1273 K is much faster than that at 1073 K; however, the oxidation kinetics are similar. During heating up, TiO2 scale forms initially on the compound surface at about 973 K, and then Al2O3 scale forms at about 1273 K. For the isothermal heating, TiO2 scale slowly grows up at 1073 K, while at 1273 K both TiO2 and Al2O3 scales grow up drastically. The outer oxide scale consists of TiO2 and the inner one consists of a mixture of TiO2 and Al2O3. The volume of Al2O3, which forms after TiO2 formation at the initial stage of oxidation, is larger at an area adjacent to the oxide-compound interface.

Original languageEnglish
Pages (from-to)1067-1073
Number of pages7
JournalJournal of Materials Science
Issue number4
Publication statusPublished - 1993 Jan
Externally publishedYes

ASJC Scopus subject areas

  • General Materials Science
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'High-temperature oxidation process of intermetallic compound Ti-42 at% Al'. Together they form a unique fingerprint.

Cite this