Influence of multiple oxide (Cr2O3/Nb2O5) addition on the sorption kinetics of MgH2

Aep Patah, Akito Takasaki, Janusz S. Szmyd

Research output: Contribution to journalArticlepeer-review

94 Citations (Scopus)


The influence of multiple additions of two oxides, Cr2O3 and Nb2O5, as additives on the hydrogen sorption kinetics of MgH2 after milling was investigated. We found that the desorption kinetics of MgH2 were improved more by multiple oxide addition than by single addition. Even for the milled MgH2 micrometric size powders, the high hydrogen capacity with fast kinetics were achieved for the powders after addition of 0.2 mol% Cr2O3 + 1 mol% Nb2O5. For this composition, the hydride desorbed about 5 wt.% hydrogen within 20 min and absorbed about 6 wt.% in 5 min at 300 °C. Furthermore, the desorption temperature was decreased by 100 °C, compared to MgH2 without any oxide addition, and the activation energy for the hydrogen desorption was estimated to be about 185 kJ mol-1, while that for MgH2 without oxide was about 206 kJ mol-1.

Original languageEnglish
Pages (from-to)3032-3037
Number of pages6
JournalInternational Journal of Hydrogen Energy
Issue number7
Publication statusPublished - 2009 Apr


  • Hydrogen sorption
  • Kinetics
  • Magnesium hydride
  • Mechanical milling
  • Metal oxides

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology


Dive into the research topics of 'Influence of multiple oxide (Cr2O3/Nb2O5) addition on the sorption kinetics of MgH2'. Together they form a unique fingerprint.

Cite this