Investigation on grown-in defects in CZ-Si crystal under slow pulling rate

Jun Furukawa, Hideo Tanaka, Yuji Nakada, Naoki Ono, Hiroyuki Shiraki

Research output: Contribution to journalConference articlepeer-review

16 Citations (Scopus)


The formation process of a dislocation cluster outside the oxidation-induced stacking fault (OSF) -ring region during Czochralski (CZ) silicon crystal growth was investigated using a quenching and in situ annealing technique. Dislocation clusters were determined to be interstitial type from inside-outside contrast analysis of the transmission electron microscope (TEM) image. From the quenching experiment, the clustering temperature of dislocations which were formed by supersaturated self-interstitials and/or small dislocation loops was found to be about 1000 °C during growth. Furthermore, the characteristic axitial distribution of dislocation size was observed in the halted crystal. This could be explained by the change in concentration of supersaturated self-interstitials and the clustering of dislocations due to the enhancement of diffusion of point defects.

Original languageEnglish
Pages (from-to)26-30
Number of pages5
JournalJournal of Crystal Growth
Issue number1
Publication statusPublished - 2000 Mar 1
Externally publishedYes
Event8th International Conference on Defects-Recognition, Imaging and Physics in Semiconductors - Narita, Jpn
Duration: 1999 Sept 151999 Sept 18

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry


Dive into the research topics of 'Investigation on grown-in defects in CZ-Si crystal under slow pulling rate'. Together they form a unique fingerprint.

Cite this