Optimization of processing conditions towards high trapped fields in MgB2 bulks

M. Muralidhar, K. Inoue, M. R. Koblischka, M. Tomita, M. Murakami

Research output: Contribution to journalArticlepeer-review

53 Citations (Scopus)


The present investigation focuses on the effects of various sintering temperatures on the critical current densities and the trapped field values of disk-shaped bulk MgB2 superconductors fabricated with a simple solid state reaction. The samples were prepared by varying the sintering temperature from 750 to 950 °C in pure Ar atmosphere. Scanning electron microscopy (SEM) and X-ray diffraction analyses showed that single phase and homogenous MgB 2 bulks are produced in using sintering temperatures in the range of 750-825 °C. The samples sintered at 775 °C showed the highest critical current density (Jc) values of 250 kA/cm2 at 10 K and 181 kA/cm2 at 20 K in self field. We also measured the trapped field values at 20 K for bulk MgB2 samples 20 mm in diameter and 7 mm in thickness, sintered at temperatures in the range of 700-950 °C with the same sintering duration of 3 h. Almost all the samples exhibited the trapped field values higher than 1 T, which shows the high potential of sintered MgB 2 bulk materials as trapped field magnets. The highest value of 1.51 T at 20 K was achieved in the MgB2 sample sintered at 775 °C, reflecting its high pinning performance and homogeneous microstructure.

Original languageEnglish
Pages (from-to)102-109
Number of pages8
JournalJournal of Alloys and Compounds
Publication statusPublished - 2014 Sept 25


  • Flux pinning
  • Microstructure analysis
  • Trapped field magnets

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry


Dive into the research topics of 'Optimization of processing conditions towards high trapped fields in MgB2 bulks'. Together they form a unique fingerprint.

Cite this