T1 - A new oxychloride, Ba2CuO2Cl2, prepared under high pressure
AU - Tatsuki, T.
AU - Tokiwa-Yamamoto, A.
AU - Tamura, T.
AU - Moriwaki, Y.
AU - Wu, X. J.
AU - Adachi, S.
AU - Tanabe, K.
N1 - Funding Information:
The authorsw ould like to expresst heir deep gratitudeto I. TerasakiK, . Nakanishoi f SRL-ISTEC and to L.L. Miller of Ames LaboratoryI,o wa State Universityf or fruitful discussion.T his work was supportedb y NEDO for the R&D of Industrial Sciencea ndT echnologFyr ontierP rogram.
PY - 1996/7/10
Y1 - 1996/7/10
N2 - We synthesized a new copper-oxychloride, Ba2CuO2Cl2, from BaCl2, BaO2 and Cu-metal powders under a high pressure of 6 GPa at 1000°C. X-ray powder diffraction and TEM observation indicated that Ba2CuO2Cl2 crystallizes in a tetragonal K2NiF4 structure with lattice parameters of a = 4.1026(3) Å and c = 16.442(1) Å. It was found from iodometric titration and SEM-EDX analysis that the average valence of the Cu ions is +1.8 and 10% chlorine is deficient.
AB - We synthesized a new copper-oxychloride, Ba2CuO2Cl2, from BaCl2, BaO2 and Cu-metal powders under a high pressure of 6 GPa at 1000°C. X-ray powder diffraction and TEM observation indicated that Ba2CuO2Cl2 crystallizes in a tetragonal K2NiF4 structure with lattice parameters of a = 4.1026(3) Å and c = 16.442(1) Å. It was found from iodometric titration and SEM-EDX analysis that the average valence of the Cu ions is +1.8 and 10% chlorine is deficient.
UR - http://www.scopus.com/inward/record.url?scp=0030181688&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0030181688&partnerID=8YFLogxK
U2 - 10.1016/0921-4534(96)00332-2
DO - 10.1016/0921-4534(96)00332-2
M3 - Article
AN - SCOPUS:0030181688
SN - 0921-4534
VL - 265
SP - 323
EP - 327
JO - Physica C: Superconductivity and its Applications
JF - Physica C: Superconductivity and its Applications
IS - 3-4
ER -