TY - JOUR
T1 - Comparative study of the flux pinning by columnar defects in high-Tc superconductors
AU - Chikumoto, N.
AU - Konczykowski, M.
AU - Kishio, K.
AU - Murakami, M.
PY - 1997/8
Y1 - 1997/8
N2 - Columnar defects are introduced to single crystals of Nd123, La214 and Bi2212 by means of 5.8-GeV Pb-ion irradiation. After the irradiation, all samples showed the enhancement of the hysteresis width in a low field range, B < BΦ. However, there are some differences in the pinning characteristics. Both irradiated Nd123 and La214 samples exhibit 'peak effect' in the magnetization curve, which is not observed in irradiated Bi2212 sample. The observed peak effect is likely to orginate from the 'matching effect'.
AB - Columnar defects are introduced to single crystals of Nd123, La214 and Bi2212 by means of 5.8-GeV Pb-ion irradiation. After the irradiation, all samples showed the enhancement of the hysteresis width in a low field range, B < BΦ. However, there are some differences in the pinning characteristics. Both irradiated Nd123 and La214 samples exhibit 'peak effect' in the magnetization curve, which is not observed in irradiated Bi2212 sample. The observed peak effect is likely to orginate from the 'matching effect'.
UR - http://www.scopus.com/inward/record.url?scp=0031208653&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0031208653&partnerID=8YFLogxK
U2 - 10.1016/S0921-4534(97)01183-0
DO - 10.1016/S0921-4534(97)01183-0
M3 - Article
AN - SCOPUS:0031208653
SN - 0921-4534
VL - 282
SP - 2143
EP - 2144
JO - Physica C: Superconductivity and its applications
JF - Physica C: Superconductivity and its applications
IS - PART 4
ER -