Effect of Gd addition on the superconducting properties of (Nd-Sm-Eu)123 system

M. Muralidhar, M. Murakami

研究成果: Article査読

17 被引用数 (Scopus)

抄録

Bulk (Nd, Sm, Eu)1-xGdxBa2Cu3 Oy superconductors in which the Gd content x ranged from 0 to 0.25, were grown by the oxygen-controlled-melt-growth (OCMG) method. X-ray diffraction results show that the main phase is RE123 with a small amount of the second phase. SQUID measurements on the oxygenated samples showed that a small amount of Gd123 addition to (Nd, Sm, Eu)123 increased Tc and made the superconducting transition sharper. All the samples, except the Gd-free one, exhibited the secondary peak effect in the magnetization curves, which shows that the field-induced pinning is active, like the other RE123 fabricated by the OCMG process. The critical current density also increased with Gd addition, however, no systematic change was observed with the amount of Gd addition. A peak Jc value of 60,000 A/cm2 was recorded with an applied field of 1.2 T (H//c) at 77 K. The results suggest that, in the (Nd, Sm, Eu)123 system the addition of Gd is effective in achieving high Tc and a large Jc.

本文言語English
ページ(範囲)127-131
ページ数5
ジャーナルApplied Superconductivity
5
1-6
DOI
出版ステータスPublished - 1997
外部発表はい

ASJC Scopus subject areas

  • 工学一般
  • 物理学および天文学一般

フィンガープリント

「Effect of Gd addition on the superconducting properties of (Nd-Sm-Eu)123 system」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル