T1 - Effect of Y-Ba-Cu-O-M (M = Zr, Sn and Ce) addition on the superconducting properties of melt-textured Y123 bulk
AU - Nariki, S.
AU - Mogi, A.
AU - Tanaka, H.
AU - Sakai, N.
AU - Murakami, M.
AU - Hirabayashi, I.
AU - Takizawa, T.
N1 - Copyright:
Copyright 2008 Elsevier B.V., All rights reserved.
PY - 2005/10/1
Y1 - 2005/10/1
N2 - We investigated the effect of Y2Ba4CuMO10 (M = Zr, Sn and Ce) addition on the superconducting properties of melt-textured Y123 bulk materials. Melt-textured Zr-doped Y123 bulk materials were fabricated from the mixed powders of Y123 and Y2Ba4CuZrO 10. As an initial attempt, Tc of the sample exhibited a low value of 86 K. However it was improved to be 90.5 K by addition of a small amount of Pt. The dispersion of fine Y2Ba4CuZrO 10 inclusions was observed in the melt-textured samples. The critical current density was enhanced with increasing the amount of Zr-phase particles. The Y2Ba4CuMO10 (M = Sn and Ce) added Y123 bulk superconductors were also fabricated and their microstructures and superconducting properties were investigated. When the Y2Ba 4CuCeO10 was employed, BaCeO3 particles were dispersed in the melt-textured bulk samples.
AB - We investigated the effect of Y2Ba4CuMO10 (M = Zr, Sn and Ce) addition on the superconducting properties of melt-textured Y123 bulk materials. Melt-textured Zr-doped Y123 bulk materials were fabricated from the mixed powders of Y123 and Y2Ba4CuZrO 10. As an initial attempt, Tc of the sample exhibited a low value of 86 K. However it was improved to be 90.5 K by addition of a small amount of Pt. The dispersion of fine Y2Ba4CuZrO 10 inclusions was observed in the melt-textured samples. The critical current density was enhanced with increasing the amount of Zr-phase particles. The Y2Ba4CuMO10 (M = Sn and Ce) added Y123 bulk superconductors were also fabricated and their microstructures and superconducting properties were investigated. When the Y2Ba 4CuCeO10 was employed, BaCeO3 particles were dispersed in the melt-textured bulk samples.
KW - Critical current density
KW - Melt-textured bulk
KW - Microstructure Y-Ba-Cu-O
KW - Y BaCuMO
UR - http://www.scopus.com/inward/record.url?scp=25644459965&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=25644459965&partnerID=8YFLogxK
U2 - 10.1016/j.physc.2005.02.063
DO - 10.1016/j.physc.2005.02.063
M3 - Conference article
AN - SCOPUS:25644459965
SN - 0921-4534
VL - 426-431
SP - 537
EP - 542
JO - Physica C: Superconductivity and its applications
JF - Physica C: Superconductivity and its applications
IS - I
T2 - Proceedings of the 17th International Symposium on Superconductivity (ISS 2004) Advances in Supeconductivity
Y2 - 23 November 2004 through 25 November 2004
ER -