Field trapping property of Gd-Ba-Cu-O bulk superconductor 140 mm in diameter

N. Sakai, M. Kita, S. Nariki, M. Muralidhar, K. Inoue, I. Hirabayashi, M. Murakami

研究成果: Article査読

31 被引用数 (Scopus)


We have studied field trapping ability of single grain Gd-Ba-Cu-O bulk superconductor 140 mm in diameter, which was fabricated by using Gd2BaO4 and Ba-Cu-O phase as raw materials. The distribution of the trapped magnetic field showed single domain without serious weak links, when the bulk was field-cooled in 1 T at liquid nitrogen temperature. The maximum trapped magnetic field at 77 K and 65 K were 2.30 T and 3.66 T respectively, when a field of 4 T was applied. From the distribution measurements of magnetic field, it was confirmed that a large amount of flux can be trapped in this large bulk. It was also confirmed that magnetic field can reach a longer distance in a larger bulk than smaller diameter samples.

ジャーナルPhysica C: Superconductivity and its applications
出版ステータスPublished - 2006 10月 1

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学


「Field trapping property of Gd-Ba-Cu-O bulk superconductor 140 mm in diameter」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。