Fracture behavior of micro-sized Ni-P amorphous alloy specimens

Y. Ichikawa, S. Maekawa, K. Takashima, M. Shimojo, Y. Higo, M. V. Swain

研究成果: Conference article査読

17 被引用数 (Scopus)


Fracture behavior of micro-sized Ni-P Amorphous alloy specimens has been investigated using a newly developed mechanical testing machine. Specimens with dimensions of 10 × 12 × 50 μm were prepared by focused ion beam machining. Two types of specimens with different crack geometries were prepared. One specimen has a notch with root radius is 0.25 μm and the other has a fatigue pre-crack. The shapes of the load-displacement curves are different for each type of specimen. The fracture strength of the specimens with a notch is higher than that with a fatigue pre-crack and the fracture surfaces of the specimens are also different for each type of specimen. This may be due to the difference in stress concentration at the crack (notch) tip, and indicates that even a notch with a root radius of 0.25 μm is not able to be regarded as a crack for micro-sized specimens. Therefore, the introduction of a fatigue pre-crack is essential for the evaluation of fracture toughness for such micro-sized specimens.

ジャーナルMaterials Research Society Symposium - Proceedings
出版ステータスPublished - 2000
イベントMaterials Science of Microelectromechanical Systems (MEMS) Devices II - Boaton, MA, USA
継続期間: 1999 11月 291999 12月 1

ASJC Scopus subject areas

  • 材料科学一般
  • 凝縮系物理学
  • 材料力学
  • 機械工学


「Fracture behavior of micro-sized Ni-P amorphous alloy specimens」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。