Hydrogen permeation through an Al-0.2 at% Mg alloy

Akito Takasaki, Yoshio Furuya, Takao Kino

研究成果: Conference article査読

1 被引用数 (Scopus)


The diffusion of hydrogen in an Al-0.2 at% Mg alloy at temperatures between 625 K and 773 K has been measured by a gas permeation technique, in which the permeation run for the sample was repeated for many times at high temperatures. Because Mg trapped hydrogen, the permeation rate for the Al-0.2 at% Mg alloy was lowered than that for an pure Al for early permeation runs. After heavily repeated runs, however, Mg was transported to the sample surface at the hydrogen reservoir side and was no loner present in the alloy except on the surface, and the permeation rate abruptly increased. The state of Mg on the surface could be a ternary oxide which consists of Mg, Al and O. The diffusivity of the Al-0.2 at% Mg after heavily repeated permeation runs were also determined and the activation energy of hydrogen diffusion was estimated to be 0.25 eV.

ジャーナルMaterials Science Forum
出版ステータスPublished - 2000
イベントThe 7th International Conference ICCA7 - 'Aluminium Alloys: 'Their Physical and Mechanical Properties' - Charlottesville, VA, USA
継続期間: 2000 4月 92000 4月 14

ASJC Scopus subject areas

  • 材料科学一般
  • 凝縮系物理学
  • 材料力学
  • 機械工学


「Hydrogen permeation through an Al-0.2 at% Mg alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。