Influence of carbon addition to Fe-Mn-Si type alloy on the structure and shape memory effect

Witold Prendota, Kamil Goc, Shunsuke Miyazawa, Akito Takasaki, Damian Rybicki, Czeslaw Kapusta

研究成果: Article査読

2 被引用数 (Scopus)


The study presented is focused on the influence of carbon addition on properties of the Fe-Mn-Si type intelligent materials with basic composition of Fe64Mn30Si6 (wt. %). Three alloys were prepared, starting from elemental powders, with 0, 0.1, and 0.3 wt. % of carbon, at corresponding silicon content reduction. For the synthesis, the mechanical alloying, sintering, and annealing were applied. Further process involved deformation and subsequent heating in a furnace. High temperature X-ray diffraction patterns, obtained at room temperature and up to 600°C, showed evolution of α′, γ, and ϵ phase peaks. The study revealed that a small carbon addition (of 0.1 wt. %), could increase shape recovery stress, even up to 1.8% after one cycle of training. The higher carbon content leads to a deterioration of the property. Also, relative density differences are observed between the sintered Fe64Mn30Si6 (wt. %) alloys with before/after annealing with/without mechanical alloying involvement.

ジャーナルAdvances in Materials Science and Engineering
出版ステータスPublished - 2018

ASJC Scopus subject areas

  • 材料科学(全般)
  • 工学(全般)


「Influence of carbon addition to Fe-Mn-Si type alloy on the structure and shape memory effect」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。