TY - JOUR
T1 - Influence of rare earth additives and boron component on electrical conductivity of sodium rare earth borate glasses
AU - Nakayama, Susumu
AU - Watanabe, Takamitsu
AU - Asahi, Taro
AU - Kiyono, Hajime
AU - Aung, Yan Lin
AU - Sakamoto, Masatomi
PY - 2010/12
Y1 - 2010/12
N2 - Sodium rare earth borate glasses (Na2O)35.7(RE 2O3)7.2(B2O3) 57.1 (RE = Sm, Gd, Dy, Ho, Y, Er, and Yb), were prepared from a mixture of Na2CO3, RE2O3 and B 2O3, and their properties as an Na+ ionic conductor were investigated. Density increased with increasing atomic weight of RE. Crystallization temperature and crystal melting temperature of the present borate system was lower than that of the previously reported silicate and germanate system. Results of the 11B NMR measurement suggested that half of all boron atoms are coordinated by four oxide ions to give a [BO 4] tetrahedral unit and the others are coordinated by three oxide ions to give a [BO3] planar triangular unit. The electrical conductivity slightly decreased with increasing the ionic radius of RE 3+. (Na2O)35.7(Y2O3) 7.2(B2O3)57.1 glass exhibited the electrical conductivity which is about one order of magnitude lower than those of the previously reported (Na2O)35.7(Y2O 3)7.2(SiO2)57.1 and (Na 2O)35.7(Y2O3)7.2(GeO 2)57.1 glasses. It was assumed that this lower electrical conductivity is due to the lower content of Na+ ions as conduction species in the former glass, compared with the latter two glasses.
AB - Sodium rare earth borate glasses (Na2O)35.7(RE 2O3)7.2(B2O3) 57.1 (RE = Sm, Gd, Dy, Ho, Y, Er, and Yb), were prepared from a mixture of Na2CO3, RE2O3 and B 2O3, and their properties as an Na+ ionic conductor were investigated. Density increased with increasing atomic weight of RE. Crystallization temperature and crystal melting temperature of the present borate system was lower than that of the previously reported silicate and germanate system. Results of the 11B NMR measurement suggested that half of all boron atoms are coordinated by four oxide ions to give a [BO 4] tetrahedral unit and the others are coordinated by three oxide ions to give a [BO3] planar triangular unit. The electrical conductivity slightly decreased with increasing the ionic radius of RE 3+. (Na2O)35.7(Y2O3) 7.2(B2O3)57.1 glass exhibited the electrical conductivity which is about one order of magnitude lower than those of the previously reported (Na2O)35.7(Y2O 3)7.2(SiO2)57.1 and (Na 2O)35.7(Y2O3)7.2(GeO 2)57.1 glasses. It was assumed that this lower electrical conductivity is due to the lower content of Na+ ions as conduction species in the former glass, compared with the latter two glasses.
KW - C. Ionic conductivity
KW - C. Thermal properties
KW - D. Glass
UR - http://www.scopus.com/inward/record.url?scp=77957695294&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=77957695294&partnerID=8YFLogxK
U2 - 10.1016/j.ceramint.2010.07.026
DO - 10.1016/j.ceramint.2010.07.026
M3 - Article
AN - SCOPUS:77957695294
SN - 0272-8842
VL - 36
SP - 2323
EP - 2327
JO - Ceramics International
JF - Ceramics International
IS - 8
ER -