Magnetic characterization of bulk C-added MgB 2

Alex Wiederhold, Michael R. Koblischka, Miryala Muralidhar, Masato Murakami, Uwe Hartmann

研究成果: Chapter


In order to find a cheap and efficient way to produce high performance bulk MgB 2 superconductors, a series of samples produced with different contents of carbon-coated, nanometer-sized amorphous boron was prepared to improve the magnetic properties. Therefore, a single-step solid-state reaction at the optimal reaction temperature of 805°C for 3 h in pure argon atmosphere was used. Small pieces cut from the bulk were characterized by magnetic hysteresis loop measurements in magnetic fields up to ± 7 T at temperatures ranging from 5 to 35 K using a physical property measurement system (PPMS). Critical current densities and flux pinning forces were calculated from the magnetization data. The pinning force data of all samples were compared using the pinning force scaling approach. The peak positions, h0, were found at h 0 ∼ 0.2, indicating a dominant flux pinning at the grain boundaries for samples with 50% and 30% carbon-coated boron, while the Eisterer scaling reveals a peak position of 0.44 for the 10% sample, which indicates pinning at point defects.

ホスト出版物のタイトルHigh-Temperature Superconductors
ホスト出版物のサブタイトルOccurrence, Synthesis and Applications
出版社Nova Science Publishers, Inc.
出版ステータスPublished - 2018 1月 1

ASJC Scopus subject areas

  • 工学(全般)
  • 材料科学(全般)


「Magnetic characterization of bulk C-added MgB 2」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。