Melt-processed Sm-Ba-Cu-O superconductors trapping strong magnetic field

H. Ikuta; A. Mase; Y. Yanagi; M. Yoshikawa; Y. Itoh; T. Oka; U. Mizutani

doi:10.1088/0953-2048/11/11/001

Melt-processed Sm-Ba-Cu-O superconductors trapping strong magnetic field

H. Ikuta, A. Mase, Y. Yanagi, M. Yoshikawa, Y. Itoh, T. Oka, U. Mizutani

研究成果: Article › 査読

146 被引用数 (Scopus)

抄録

Large c-axis-oriented Sm-Ba-Cu-O bulk superconductors were prepared using the melt-process technique in a reduced oxygen atmosphere. Single-domain samples up to 36 mm in diameter were successfully and reproducibly synthesized with no severe weak-link within the samples. The trapped magnetic field at the open surface of the sample was recorded as 8.0 T at 40 K when measured immediately after the external field was swept down to zero. This value far exceeds that of a melt-processed Y-Ba-Cu-O with a similar size.

本文言語	English
ページ（範囲）	1345-1347
ページ数	3
ジャーナル	Superconductor Science and Technology
巻	11
号	11
DOI	https://doi.org/10.1088/0953-2048/11/11/001
出版ステータス	Published - 1998 11月
外部発表	はい

ASJC Scopus subject areas

セラミックおよび複合材料
凝縮系物理学
金属および合金
電子工学および電気工学
材料化学

文献へのアクセス

10.1088/0953-2048/11/11/001

他のファイルとリンク

引用スタイル

@article{a2785faef190433d8002212c9eefeefd,

title = "Melt-processed Sm-Ba-Cu-O superconductors trapping strong magnetic field",

abstract = "Large c-axis-oriented Sm-Ba-Cu-O bulk superconductors were prepared using the melt-process technique in a reduced oxygen atmosphere. Single-domain samples up to 36 mm in diameter were successfully and reproducibly synthesized with no severe weak-link within the samples. The trapped magnetic field at the open surface of the sample was recorded as 8.0 T at 40 K when measured immediately after the external field was swept down to zero. This value far exceeds that of a melt-processed Y-Ba-Cu-O with a similar size.",

author = "H. Ikuta and A. Mase and Y. Yanagi and M. Yoshikawa and Y. Itoh and T. Oka and U. Mizutani",

year = "1998",

month = nov,

doi = "10.1088/0953-2048/11/11/001",

language = "English",

volume = "11",

pages = "1345--1347",

journal = "Superconductor Science and Technology",

issn = "0953-2048",

publisher = "IOP Publishing Ltd.",

number = "11",

}

TY - JOUR

T1 - Melt-processed Sm-Ba-Cu-O superconductors trapping strong magnetic field

AU - Ikuta, H.

AU - Mase, A.

AU - Yanagi, Y.

AU - Yoshikawa, M.

AU - Itoh, Y.

AU - Oka, T.

AU - Mizutani, U.

PY - 1998/11

Y1 - 1998/11

N2 - Large c-axis-oriented Sm-Ba-Cu-O bulk superconductors were prepared using the melt-process technique in a reduced oxygen atmosphere. Single-domain samples up to 36 mm in diameter were successfully and reproducibly synthesized with no severe weak-link within the samples. The trapped magnetic field at the open surface of the sample was recorded as 8.0 T at 40 K when measured immediately after the external field was swept down to zero. This value far exceeds that of a melt-processed Y-Ba-Cu-O with a similar size.

AB - Large c-axis-oriented Sm-Ba-Cu-O bulk superconductors were prepared using the melt-process technique in a reduced oxygen atmosphere. Single-domain samples up to 36 mm in diameter were successfully and reproducibly synthesized with no severe weak-link within the samples. The trapped magnetic field at the open surface of the sample was recorded as 8.0 T at 40 K when measured immediately after the external field was swept down to zero. This value far exceeds that of a melt-processed Y-Ba-Cu-O with a similar size.

UR - http://www.scopus.com/inward/record.url?scp=0032204824&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0032204824&partnerID=8YFLogxK

U2 - 10.1088/0953-2048/11/11/001

DO - 10.1088/0953-2048/11/11/001

M3 - Article

AN - SCOPUS:0032204824

SN - 0953-2048

VL - 11

SP - 1345

EP - 1347

JO - Superconductor Science and Technology

JF - Superconductor Science and Technology

IS - 11

ER -

Melt-processed Sm-Ba-Cu-O superconductors trapping strong magnetic field

抄録

ASJC Scopus subject areas

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル