Optimization of YbBa2Cu3Oy Thick Film Formation on MgO Substrates

S. Kawata, M. Muralidhar, M. Jirsa, K. Inoue, M. Murakami

研究成果: Conference article査読


We optimized the formation process of the YbBa2Cu3Oy superconducting thick film prepared from the mixture of Yb2BaO4, BaCuO2, and CuO. Thick films of this composite were sintered at various temperatures between 800 °C and 1025 °C and held for 10 minutes in air, then rapidly quenched in liquid nitrogen. The samples were characterized by XRD, SEM, and magnetization measurements. The XRD analysis indicated that the Yb-123 phase started to form above 800 °C, with optimum at 825 °C. At even higher temperatures (900 °C and 975 °C) the secondary phase and liquid phase predominantly formed. Based on these results, we fabricated good quality YbBa2Cu3Oy thick films on an MgO substrate utilizing a double step heating process. According to XRD measurements the Yb-123 films were c-axis oriented, with Tc (onset) 87 K, and high critical current density around 24 kA/cm2 at 77 K, H//c-axis. The Yb-123 superconducting thick films on the MgO substrates are considered as the first step to the production of silver sheathed tapes, an advanced analogue to the Bi-2223 system.

ジャーナルPhysics Procedia
出版ステータスPublished - 2016
イベント28th International Symposium on Superconductivity, ISS 2015 - Tokyo, Japan
継続期間: 2015 11月 162015 11月 18

ASJC Scopus subject areas

  • 物理学および天文学一般


「Optimization of YbBa2Cu3Oy Thick Film Formation on MgO Substrates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。