Oxidation of HIPed TiC ceramics in dry O2, wet O2, and H2O atmospheres

S. Shimada, T. Onuma, H. Kiyono, M. Desmaison

研究成果: Article査読

18 被引用数 (Scopus)


Isothermal oxidation of dense TiC ceramics, fabricated by hot-isostatic pressing at 1630°C and 195 MPa, was performed in Ar/O2 (dry oxidation), Ar/O2/H2O (wet oxidation), and Ar/H 2O (H2O oxidation) at 900°-1200°C. The weight change measurements of the TiC specimen showed that the dry, wet, and H 2O oxidation at 850°-1000°C is represented by a one-dimensional parabolic rate equation, while the oxidation in the three atmospheres at 1100°and 1200°C proceeds linearly. Cross-sectional observation showed that the dry oxidation produces a lamellar TiO2 scale consisting of many thin layers, about 5 μm thick, containing many pores and large cracks, while H2O-containing oxidation decreases pores in number and diminishes cracks in scales. Gas evolution of CO2 and H2 with weight change measurement was simultaneously followed by heating the TiC to 1400°C in the three atmospheres. Cracking in the TiO 2 scale accompanied CO2 evolution, and the H 2O-containing oxidation produced a small amount of H2. A piece of single crystal TiC was oxidized in 16O2/H 218O to reveal the contribution of O from H2O to the oxidation of TiC by secondary ion mass spectrometry.

ジャーナルJournal of the American Ceramic Society
出版ステータスPublished - 2006 4月

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 材料化学


「Oxidation of HIPed TiC ceramics in dry O2, wet O2, and H2O atmospheres」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。