Preparation of melt-textured NdBa2Cu3Oy bulk with Nd4Ba2Cu2O10 addition

A. Takagi, T. Yamazaki, T. Oka, Y. Yanagi, Y. Itoh, M. Yoshikawa, Y. Yamada, U. Mizutani

研究成果: Article査読

31 被引用数 (Scopus)


The NdBa2Cu3Oy (Nd123) bulk superconductor, to which Nd4Ba2Cu2O10 (Nd422) particles were intentionally added, was prepared through the so-called MMTG process in Ar (99% purity) flowing atmosphere at an ambient pressure. The quasi-single crystal thus grown was about 1 cm × 1 cm × 1 cm in dimension. It turned out that the Nd422 particles were uniformly distributed in the Nd123-phase matrix in a fashion similar to the distribution of the intentionally added Y211 particles in the Y123 phase matrix. The superconducting transition temperature Tc for the sample subjected to post-annealing in oxygen atmosphere was 94 K. The critical current density Jc was determined to be 45 000 A/cm2 at 77 K and 1 T, when the field was applied parallel to the c-axis of the sample. To the best of our knowledge, the Jc value is the highest and the size of the quasi-single crystal is the largest in the melt-textured Nd123 bulk superconductors so far reported.

ジャーナルPhysica C: Superconductivity and its applications
出版ステータスPublished - 1995 8月 15

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学


「Preparation of melt-textured NdBa2Cu3Oy bulk with Nd4Ba2Cu2O10 addition」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。