T1 - Structural study on the (Hg,Tl)-Ba-(Ca,Y)-Cu-O system by XRD and TEM
AU - Wu, X. J.
AU - Tokiwa-Yamamoto, A.
AU - Tatsuki, T.
AU - Adachi, S.
AU - Tanabe, K.
N1 - Copyright:
Copyright 2018 Elsevier B.V., All rights reserved.
PY - 1997/8
Y1 - 1997/8
N2 - Superconducting (Hg,Tl)-O double layer compound samples were prepared by a high-pressure synthesis technique. Some samples have the composition of (Hg0.7,Tl0.3)2Ba2(Ca x,Y1-x)Cu2O8-2δ and are nearly single phase when x=0.1, 0.2, 0.4 and 0.6. The crystal structure of these samples was determined by X-ray Rietveld refinement. On the other hand, several new intergrowth phases were discovered in Y-free Hg(Tl)-Ba-Ca-Cu-O samples by TEM observation. Based on the TEM observation, symmetry and super-lattice parameters for the new phases were determined and structural models were proposed.
AB - Superconducting (Hg,Tl)-O double layer compound samples were prepared by a high-pressure synthesis technique. Some samples have the composition of (Hg0.7,Tl0.3)2Ba2(Ca x,Y1-x)Cu2O8-2δ and are nearly single phase when x=0.1, 0.2, 0.4 and 0.6. The crystal structure of these samples was determined by X-ray Rietveld refinement. On the other hand, several new intergrowth phases were discovered in Y-free Hg(Tl)-Ba-Ca-Cu-O samples by TEM observation. Based on the TEM observation, symmetry and super-lattice parameters for the new phases were determined and structural models were proposed.
UR - http://www.scopus.com/inward/record.url?scp=0031207196&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0031207196&partnerID=8YFLogxK
U2 - 10.1016/S0921-4534(97)00540-6
DO - 10.1016/S0921-4534(97)00540-6
M3 - Article
AN - SCOPUS:0031207196
SN - 0921-4534
VL - 282-287
SP - 889
EP - 890
JO - Physica C: Superconductivity and its applications
JF - Physica C: Superconductivity and its applications
IS - PART 2
ER -